Process for producing zirconium based granules

ABSTRACT

Zirconium based granules are produced by the steps of forming an aqueous solution of a zirconium compound such as zirconium acetate, combining the aqueous solution with a phase stabilizer, and then heating the solution to evaporation at a temperature below about 180° C. preferably below thereby forming amorphous zirconium based granules. 
     In an alternate embodiment, an alcohol solution of a zirconium compound such as zirconium propoxide in propanol is acidified and hydrolyzed with water. The partially or fully hydrolyzed zirconium complex is mixed with a phase stabilizer to form a homogeneous solution. The solution is then subjected to evaporation at a temperature below about 180° C. or below to form amorphous zirconium based granules. 
     Zirconia fibers are produced by making aqueous solution of the amorphous zirconium based granules containing the phase stabilizer to the desired viscosity, fiberizing the solution, and finally converting the fibers under appropriate conditions.

This Application is a Continuation-in-Part of application Ser. No.07/065,809 filed June 19, 1987, now abandoned.

FIELD OF THE INVENTION

This invention relates to novel processes for the production of ceramicgranules and more particularly, it relates to novel processes for theproduction of amorphous zirconium based granules. This invention furtherrelates to novel processes for the production of zirconium oxide fibers.

BACKGROUND OF THE INVENTION

The existence of ceramic oxide, e.g. alumina and zirconia, powders andfibers is known to those skilled in the art.

U.S. Pat. No. 3,180,741 discloses a conventional process for thepreparation of ceramic (refractory) fibers. The conventional processinvolves the steps of forming a dilute solution of a ceramic oxideprecursor such as zirconium acetate followed by concentrating thesolution to the desired viscosity. The concentrated solution of desiredviscosity is then fiberized with the resulting fibers subsequentlyheated in an oxygen containing atmosphere to form an oxide fiber. Adifficulty encountered in this process is the required concentration ofthe ceramic oxide precursor solution. This is because the typical modesof concentration, e.g. vacuum evaporation and solids precipitation, arenot only time consuming and cumbersome but also if they are not properlycontrolled can lead to solutions of either too high or too low ofviscosities to subsequently fiberize. If the resulting viscosity is toohigh, the solution is difficult to spin into fibers. A solution of toolow of viscosity yields inferior fibers, if any.

U.S. Pat. No. 4,159,205 discloses that fibers made by such conventionalmethods have insufficient strength and flexibility for manyapplications.

In recent years, attempts have been made to viscosity the solution bythe addition of certain organic acids. U.S. Pat. No. 4,159,205 disclosesthat the addition of acetic acid to spinning solutions results in fiberswhich were still too brittle for many applications because of the lackof control of nucleation, grain size, phase stabilization, andcrystallization behavior. Although the use of lactic acid is disclosedas an alternative, it is possible that fibers of non-uniform crosssections, poor reproducibility, and relatively poor physical propertiescan result.

As disclosed by U.S. Pat. No. 4,619,817 there are five main methods thathave been reported to date for producing partially stabilized zirconiapowders (granules): (1) powder mixing, (2) coprecipitation anddecomposition, (3) vapor phase decomposition, (4) sol-gel processing,and (5) hydrothermal processing. As disclosed by U.S. Pat. No. 4,619,817difficulties lay in utilizing the methods in that each is specializedand therefore has its own distinct drawbacks and disadvantages.

From the foregoing discussion, it is readily apparent that each knownmethod for the production of ceramic oxide powders and fibers hasdisadvantages and drawbacks. Because of the continuing demand forceramic oxide powders and fibers, improved methods which eliminate anyof the drawbacks of the conventional methods and which are practical andeconomical to utilize would be highly advantageous.

BRIEF SUMMARY OF THE INVENTION

In accordance with the present invention, there are provided two novelprocesses for the production of water soluble, amorphous zirconium basedgranules. Each inventive method employs a starting solution of

    Zr(R).sub.4

wherein each R group individually represents either ##STR1## --OX; --NO₃; --OH; --OY; or halogen and X represents a C₁ to C₁₀ hydrocarbyl groupand Y represents halogen.

In one embodiment, an aqueous solution comprising Zr(R)₄ is formed andthen mixed with a suitable stabilizing agent, e.g. CaO, CeO₂, Y₂ O₃,MgO, SiO₂, hafnium oxide, and the like and mixtures thereof. The aqueoussolution of stabilized zirconium complex is then dried at a temperaturebelow about 180° C. to form amorphous, dried granules which contain saidphase stabilizer.

In another embodiment, an alcohol or the like solution of Zr(R)₄ isformed and then acidified and hydrolyzed, in either order, to form asolution comprising a zirconium based complex which is subsequentlymixed with a phase stabilizer. The solution is then evaporated by dryingat a temperature below about 180° C. thereby forming amorphous zirconiumbased granules which contain the phase stabilizer.

In further accordance with the present invention, processes for theproduction of zirconium oxide fibers are provided. In each embodiment,the amorphous zirconium based granules produced by the foregoingdisclosed inventive processes are formed in an aqueous solution to thedesired viscosity and are subsequently fiberized and heated undersuitable conditions of time and temperature to zirconium oxide fibers.

The inventive processes for forming zirconium based granules are easy topractice and do not carry the disadvantages of the aforementionedconventional methods. The starting materials, e.g. zirconium acetate,zirconium propoxide, zirconium oxychloride, and the like covered by thegeneral formula Zr(R)₄ are commercially readily available and are easyto make into solutions with water, alcohols, or the like. The zirconiumcompounds can be easily mixed with stabilizers and moreover, thehomogeneous solutions can very readily be evaporated to dryness and thezirconium based granules thereby formed by a simple heat treatment step.

Additionally, the inventive processes for the production of zirconiumoxide (zirconia) fibers are easy to practice and obviate the drawbacksassociated with conventional processes. The zirconia fibers are madefrom aqueous solutions of zirconium based granules which can function aszirconium oxide precursors. No cumbersome or tedious concentration stepis required and the desired viscosity range for the solution can bereadily achieved and controlled.

Consequently, fibers of uniform diameter, grain size, little or no shotcontent and reproducible properties can be produced.

Other features and aspects of the invention, as well as their benefits,will be made clear in the more detailed description of the inventionwhich follows.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a scanning electron micrograph (SEM) of zirconia fiberscontaining CaO, prepared according to the present invention; sintered inoven in air at 1250° C. for 2 hours; 200× magnification.

FIG. 2 is a scanning electron micrograph (SEM) of single zirconia fiberscontaining CaO, prepared according to the present invention; sintered inoven at 1250° C. in air for 2 hours; 15.000× magnification.

FIG. 3 is a SEM of zirconia fibers containing CaO, prepared according tothe present invention; sintered in oven at 850° C. in air for 2 hours;200× magnification;

FIG. 4 is a SEM of a single zirconia fiber containing CaO, preparedaccording to the present invention; sintered in oven at 850° C. in airfor 2 hours; 15,000× magnification.

FIG. 5 is a SEM of a single zirconia fiber containing CaO, preparedaccording to the present invention; sintered in oven at 850° C. in airfor 2 hours; 15,000× magnification.

FIG. 6 is a selected area electron diffraction (SAED) pattern ofzirconia fibers containing CaO, prepared according to the presentinvention, sintered in oven at 1000° C. in air for 2 hours.

DETAILED DESCRIPTION OF THE INVENTION

In accordance with the present invention, novel processes for theproduction of water soluble, amorphous zirconium based granules areprovided.

In one embodiment, an aqueous solution comprising a zirconium basedcompound of the formula Zr(R)₄ as defined herein earlier is prepared.Preferably the solution will contain about 1 to 99 wt % Zr(R)_(r) andmost preferably about 10 to 50 wt % Zr(R)₄ based upon the total weightof the solution.

Although water is the preferred and the most practical solvent toutilize in this embodiment, it is within the spirit and scope of thepresent invention that solvents of similar polarity to water may beutilized non-limiting example of which include dimethyl sulfoxide,acetone, acetonitrile, tetrahydrofuran, n-propanol, and butanol.

With regard to the zirconium compound of the formula

    Zr(R).sub.4

R will preferably represent ##STR2## wherein X is preferably a C₁ to C₁₀alkyl group and most preferably X represents methyl such that Zr(R)₄ iszirconium acetate.

Once the aqueous solution has been formed, the zirconium based compoundis mixed with the solution of about 2 to 15 wt %, preferably 6 to 10 wt%, of a phase stabilizing agent based upon the total weight of zirconiumoxide in solution. Suitable phase stabilizing agents are well known tothose skilled in the art of which non-limiting examples include CaO,CeO₂, Y₂ O₃, MgO, SiO₂, HfO₂, Dy₂ O₃, Yb₂ O₃ and the like.

It is also within the scope of the present invention to employ metalsalts of phase stabilizing agents, e.g. calcium hydroxide, yittriumacetate, cerium acetate, and hafnium oxychloride, which upon heatingconvert to their oxide form.

The pH of the solution once the phase stabilizing agent has been addedshould be in the range of about 2 to 7 and preferably about 2 to 5.

Zirconium based granules are then formed by heating the pH adjusted andaqueous zirconium complex containing phase stabilizer to a temperatureno greater than about 180° C., and preferably no greater than about 120°C., until all of the aqueous (or the like) solution is evaporated andthe resulting zirconia based complex containing the phase stabilizerthereby becomes granular in nature.

If the solution is heated above about 180° C., the resulting granuleswill not have good solubility in water as the hydrogen bonding in thezirconium complex will probably have been destroyed.

In an alternate embodiment, an alcohol (or the like) solution of Zr(R)₄is prepared. In this embodiment, the ZrO₂ content of the solution willpreferably be in the range of about 1 to 99 wt %, and most preferablyabout 10 to 40 wt %, based upon the total weight of the solution.

Although an alcohol is the most suitable type of solvent to be employedin the alternate embodiment, it is within the spirit and scope of thepresent invention that solvents of similar nature and polarity can beutilized non-limiting examples of which include acidified water,dimethyl sulfoxide, tetrahydrofuran, and acetone.

In this alternate embodiment of the present invention, the R group ofZr(R)₄ will preferably represent --OX wherein X preferably represents aC₁ to C₁₀ alkyl group and most preferably X represents propyl such thatZr(R)₄ is zirconium propoxide.

When R represents --OX, the alcohol solvent will preferably be of theformula R'OH wherein R' corresponds to X. For example, propanol shouldpreferably be the solvent for zirconium propoxide.

After the solution is formed, it is then acidified and hydrolyzed ineither order.

In the acidification step, the pH of the solution should be adjusted tobetween about 2 to 5, preferably about 2 to 3, with the use of anysuitable acid and preferably an organic acid such as acetic acid.

In the hydrolysis step, water is preferably added in an amount of fromabout 1 to 90 wt %, most preferably 10 to 30 wt %, based upon the totalweight of zirconium atoms in solution or otherwise in an amountsufficient to hydrolyze the solution of zirconium compound, e.g.zirconium propoxide, to the desired degree.

After acidification and hydrolysis, about 1-35 wt % phase stabilizer andpreferably about 6-10 wt % phase stabilizer is added to the solutionbased upon the total weight of ZrO₂ in the solution and the solution isthen heated to below about 180° C., and preferably below about 120° C.,to form water soluble, amorphous zirconium based granules which canfunction as zirconium oxide precursors.

In some instances a zirconium based foam or the like may develop duringthe evaporation process. Granules or flakes or the like can be readilyproduced by merely crushing or grinding the foam.

The zirconium based granules made by the inventive process have utilityas coatings for glass fibers and the like to enhance their fireresistance and alkali resistance properties and as disclosed in anotherembodiment of the present invention can be used to manufacture fibers ofzirconium oxide.

According to this embodiment of the present invention, zirconium oxide(zirconia) fibers can be readily made by first making an aqueoussolution of either zirconium based granules to the desired viscosity.Preferably, in order to get a solution which will fiberize well, theviscosity should be in the range of about 8,000 to 30,000 c.p.s. andmost preferably about 12,000 to 26,000 c.p.s.

In accordance with the invention, the liquid is fiberized by anyconvenient method such as, for example, centrifugal spinning, drawing,blowing, tack-spinning, rotary spinning, and by extrusion of the liquidthough a spinneret or suitable combinations thereof.

The fiber is then heated or sintered for a time sufficient and at atemperature sufficient to oxidize the zirconium based complex tozirconium oxide. The heating typically occurs in an oxygen containingatmosphere such as dry air or ozone. Although an oxygen containingatmosphere is typically utilized, it is thought possible that in someinstances, heating can occur in an oxygen free atmosphere since thepresence of water in the spinning solution can sometimes be sufficientto convert zirconium based compounds to oxides upon heating.

The heating or sintering temperature is preferably between about 100° C.to 1800° C. and more preferably between about 250° C. to 1250° C. Theheating time is in excess of about 15 minutes and is preferably inexcess of about 1 hour.

With regard to the phase structures of the zirconia fibers produced bythe present invention, they will be in an amorphous state until they areheated to a temperature in the range from above about 500° C. to about1100° C. at which region they are in the tetragonal crystal phase. Attemperatures from above about 1100° C. to about 1900° C. some of thefibers are still in the tetragonal phase and some will be in themonoclinic phase depending on the type of stabilizer used and attemperature above about 1900° C. they are in the cubic phase.

The following non-limiting examples serve to further illustrate thepresent invention.

EXAMPLE I

This example illustrates the preparation of amorphous zirconium hydroxyhydrogel granules from zirconium alkoxide solution, e.g. zirconiumn-propoxide.

491.34 grams of zirconium n-propoxide of 21.6 wt. % zirconium contentwere added with mixing to 791.52 grams of n-propanol to provide ahomogeneous solution. The pH was adjusted to 2-3 by the addition of198.17 grams of glacial acetic acid and finally by the addition of 1.5liters of water. The reaction mixture was mixed from 1/2 hour at roomtemperature. To 2.2 lbs. of the resulting zirconium hydroxy hydrogel(17.6 wt. % ZrO₂ content), was added approximately 6 wt. % of CaO ofcalcium acetate powder (17.96 grams) as a stabilizer.

The solution was mixed thoroughly until it became clear. Then thesolution was evaporated to dryness using a microwave oven at about 120°C. The chemical composition (wt. %) of the resulting amorphous zirconiumbased granules was as follows:

% C=16.69; % H=2.89; % Ca=9.69; % Zr=49.90.

The granules were found to be soluble in water.

EXAMPLE II

The granules prepared in Example I were heated in a microwave oven toabout 200° C. These granules were found to have poor solubility inwater.

EXAMPLE III

This example illustrates the preparation of amorphous zirconium basedgranules from zirconium acetate.

6.94 grams of commercially available Ca(OH)₂ powder were added withmixing to 250.0 grams of aqueous zirconium acetate, (21-22 wt. % ofZrO₂), to provide a clear homogeneous solution having a pH of about 4-5and an equivalent weight ratio of 10:1 of ZrO₂ to CaO and an equivalentsolids content of about 75 weight percent. The resulting aqueousdispersion was slightly cloudy on mixing but became clear whencompletely.

The solution was transferred into a suitable container and evaporated todryness using a conventional microwave oven. During the evaporation, thetemperature did not exceed 150° C.-180°° C. The resulting granules werecolorless and amorphous as shown by X-ray diffraction. An elementalanalysis of the granules showed the following composition:

% C=15.97; % H=3.02; % Ca=9.71; % Zr=50.1.

The granules were found to be soluble in water.

EXAMPLE IV

The granules prepared in Example III were heated in a microwave oven toabout 200° C. These granules were found to have poor solubility inwater.

EXAMPLE V

This example illustrates the preparation of zirconium based flakes froma zirconium oxychloride starting solution.

7.45 grams of commercial Ca(OH)₂ was added with mixing to 281.74 gramsof an aqueous zirconium oxychloride (ZrOCl₂) solution of 20% 2 w/w ZrO₂and HfO₂ and 12% w/w HCl to provide a homogeneous yellow solution havingan equivalent weight ratio of 10:1 of ZrO₂ to CaO and an equivalentsolids content of about 50 weight percent.

The solution was transferred into a suitable container and evaporated todryness using a conventional microwave oven. During the evaporation thetemperature did not exceed 150°-180° C. Upon drying a yellow foam wasformed. The foam was then crushed into small flakes.

EXAMPLE VI

The flakes prepared in Example V were heated in a microwave oven toabout 200° C. These flakes were not found to be soluble in water.

EXAMPLE VII

This example illustrates how solutions of controlled viscosity can beprepared by utilizing the amorphous granules produced by the process ofthe present invention.

Utilizing the previously disclosed procedures, amorphous zirconium basedhydroxy hydrogel granules were prepared from zirconium acetate andzirconium propoxide solutions using appropriate amounts of yittriumacetate, cerium acetate, hafnium oxychloride and colloidal silica andmixtures thereof as phase stabilizing agents. The zirconium basedsolutions containing the phase stabilizers were evaporated to granulesin a microwave oven at a temperature not exceeding 150° C.-180° C. Thefinal composition weight ratio (zirconia:stabilizing agent) of amorphousgranules was in the range of about 10:0.6-0.8.

In each instance when the prepared granules were added to water in aweight ratio of about 4:3 and placed on drum rollers, the granules werecompletely dissolved and viscosity of the resulting solution was about6,000 c.p.s. The viscosity of each solution could be adjusted to thedesired level by either adding additional granules or water.

EXAMPLE VIII

This example illustrates the production of partially or fully stabilizedZrO₂ fibers derived from a viscous precursor solution of zirconiumacetate which was treated and formed into granules by the procedure ofExample III.

The fibers were formed by feeding a viscous mass of 8,000 to 30,000centipoise to a centrifugal spinning machine with a 53/8" diameter headhaving multiple holes of 0.012" in their smallest dimension. Thespinning conditions are given in the Table I.

The fibers were removed from the collection chamber and sintered in airby placing the fibers in an electric furnace at a temperature of 250° C.for 2 hours. The 250° C. fired fibers were further fired in air in afurnace as below:

The physical properties of ZrO₂ fibers derived from Run 5 of Table I areshown in Table II.

                                      TABLE I                                     __________________________________________________________________________                                        ZrO.sub.2 Fiber                                               Box Temp °F.                                                                   Disc Temp °F.                                                                  Precursor                                          Air Ring   at the  at the  solution temp                                                                         Comments                             Viscosity                                                                           Pressure                                                                           Disc  beginning                                                                             beginning                                                                             °F. at beginning                                                               on                                Run                                                                              cps. × 10.sup.3                                                               (psig)                                                                             (Psig)                                                                              of run  of run  of run  spinning                          __________________________________________________________________________    1  23    7    7 turned                                                                            160     88      27      spun very well                                  up to 12                                                        2  22    7    11 turned                                                                           160     92      34      spun very well                                  up to 12                                                        3  24    7    7 turned                                                                            162     88      37      spun very well                                  up to 12                                                        4  9.6   7    12.5  160     89      68      spun well                         5  25    7    7 up to 12                                                                          175     88      25      spun very well                    6  23    7    12    115     98      34      spun very well                    __________________________________________________________________________

                                      TABLE II                                    __________________________________________________________________________                     Fiber (b)               X-ray diffraction, Zr                         Fiber (a)                                                                             Diameter                                                                           Surface Area (c)                                                                       Crystallite Size (d)                                                                    phase relative intens                Fiber                                                                             Firing                                                                             Density g/cm.sub.3                                                                    Microns                                                                            by BET, m.sub.2 /g                                                                     by X-ray, Angstrons                                                                     % monoclinic                                                                         % tetragonal                  __________________________________________________________________________    I   250° C.                                                                     3.103   8.586                                                                              0.1782   0         Amorphous                                2 hrs                                                                     II  500° C.                                                                     4.315   0.052                                                                              29.4535 (c)                                                                             68A°      100                              for                                                                           2 hrs                                                                     III 850° C.                                                                     4.773   3.210                                                                              0.0476   132A°                                                                            <1     >99                               for                                                                           2 hrs                                                                     IV  1000° C.                                                                    5.028   2.773                                                                              0.5517   235A°                                                                            <1     >99                               for                                                                           2 hrs                                                                     __________________________________________________________________________     Notes:                                                                        (a) Density measurements by pycnometer and water as the filling solution      (b) Measured by optical microscope and BET method                             (c) Indicates nitrogen runs due to high surface area                          (d) WarrenAverbach Crystallite size determination                             (e) The Xray analysis of the 1000° C. fired fibers revealed the        presence of                                                              

EXAMPLE IX

An aqueous solution comprising 5% zirconia was prepared by dissolving3.38 g. of zirconia precursor granules, prepared as described in ExampleIII, in 100 g. of tap water. A 0.36 g, 11.0 cm diameter fiber glass matwith binder burned off (30 minutes at 500° C.) was dipped into thesolution and on removal excess solution was drained out of the glass matby applying suction. The mat was then cured in an electric oven for 15minutes at 150° C. The weight of coating on the glass mat was found tobe 0.37 g.

An 11.0 cm diameter sample of the above inventive treated glass mat wasthen subjected to a fire test over a gas burner fitted with a circularjet of diameter 35 mm, the sample being held on a support 100 mm metalring 50 mm above the burner nozzle. The temperature of the flame at thesample position was determined as 950° C. No smoke, no fire structuredamage, and no shrinkage of the inventive treated glass mat was observedeven after 3 hours of continuous firing. Under an identical firing test,a glass mat melted within a second or two.

Reasonable modifications and variations are possible from the foregoingdisclosure without departing from either the spirit or scope of thepresent invention as defined by the claims.

I claim:
 1. A process for the production of amorphous zirconium basedgranules, said process consisting essentially of the steps of:(a) addingabout 2-15 wt % of a suitable phase stabilizer to an aqueous solution,based upon the total weight of ZrO₂ in solution, comprising a compoundof the formula Zr(R)₄, wherein each R is individually selected from thegroup consisting of ##STR3## --OX; --NO₃, halogen; --OH, or OY and Xrepresents a C₁ -C₁₀ hydrocarbyl group and Y represents a halogen, toproduce an aqueous solution having a pH in the range of about 4 to 7comprising a zirconium based complex and phase stabilizer andthereafter; (b) drying said aqueous solution comprising said zirconiumbased complex and said phase stabilizer at a temperature below about180° C. for a time a sufficient to evaporate said aqueous solutionthereby forming amorphous zirconium based granules containing said phasestabilizer.
 2. A process according to claim 1 wherein R represents##STR4## and X is a C₁ to C₁₀ alkyl group.
 3. A process according toclaim 1 wherein Zr(R)₄ is zirconium acetate.
 4. A process according toclaim 1 wherein said phase stabilizer is calcium hydroxide.